Surface Modification of 2205 Duplex Stainless Steel by Low Temperature Thermochemical Hybrid Heat Treatment at 450° C

Adenan, M.S. and Berhan, M.N. and Haruman, Esa (2014) Surface Modification of 2205 Duplex Stainless Steel by Low Temperature Thermochemical Hybrid Heat Treatment at 450° C. Advanced Materials Research, Vol845. pp. 408-411. ISSN 10226680

[thumbnail of pdf] Text (pdf)
TIN-Artikel-002 Surface Modification of 2205 Duplex Stainless Steel by Low.pdf - Published Version
Restricted to Registered users only

Download (461kB)

Abstract

An approach has been made in developing hybrid heat treatment process for improvement of surface properties of duplex stainless steel (DSS). The process was performed using horizontal tube furnace at temperature of 450° C at holding time of 4, 8, 16 and 30 hours. Carbon and nitrogen elements were simultaneously introduced onto the surface of DSS with a ratio of 5%CH4 + 25% NH3 + 70% N2. The microstructure, phase analysis, surface hardness and hardness profile were systematically assessed. Hybrid heat treatment process managed to produce diffusional layer, where longer holding time had increased the thickness of the layer and improved the surface hardness. Expanded austenite phase has been formed at specimens 8, 16 and 30 hours. Longer holding time however gradually diffused Cr2N at the ferrite grains at the substrates. From the process, it can be concluded that low temperature hybrid heat treatment be able to improve the surface hardness of DSS however concern on holding time must be highly considered

Item Type: Article
Uncontrolled Keywords: Austenite; Heat treatment; Industrial engineering; Industrial research; Stainless steel; Temperature
Subjects: Science > Physics
Science > Chemistry
Divisions: Fakultas Teknik dan Ilmu Komputer > Program Studi Teknik Industri
Depositing User: Users 2 not found.
Date Deposited: 25 Jul 2016 02:15
Last Modified: 25 Jul 2016 02:15
URI: https://repository.bakrie.ac.id/id/eprint/132

Actions (login required)

View Item View Item